BS EN 60404-6:2003

INTRODUCTION
1 Scope
2 Normative references
3 General principles of measurement
   3.1 Test specimen
   3.2 Windings
4 Temperature measurements
5 Measurement of magnetic permeability and magnetization curve
   using the voltmeter-ammeter method
   5.1 Introduction
   5.2 Apparatus and connections
   5.3 Determination of magnetic field strength
   5.4 Determination of the magnetic flux density
   5.5 Determination of the r.m.s amplitude permeability and the
       relative amplitude permeability
   5.6 Determination of magnetization curve
6 Measurement of specific total loss by the wattmeter method
   6.1 Principle of measurement
7 Measurement of magnetic properties using a digital impedance bridge
   7.1 Principle of measurement
   7.2 Apparatus
   7.3 Procedure
   7.4 Determination of the relative a.c. inductance permeability
   7.5 Determination of the specific total loss
8 Measurement of magnetic properties using digital methods
   8.1 Introduction
   8.2 Apparatus and connections
   8.3 Magnetizing current waveform
   8.4 Magnetizing winding
   8.5 Determination of the magnetic field strength
   8.6 Determination of the magnetic flux density
   8.7 Determination of the relative a.c. permeability
   8.8 Determination of a.c. magnetization curve
   8.9 Determination of the specific total loss
9 Uncertainties
10 Test report
Annex A (informative) Guidance on requirements for windings and
        instrumentation in order to minimise additional losses
Annex B (informative) Sinusoidal waveform control by digital means
Annex ZA (normative) Normative references to international
         publications with their corresponding European publications
Bibliography

Describes methods for the measurement of a.c. magnetic properties of materials in the frequency range 20 Hz to 200 kHz other than electrical steels and soft ferrites.

Specifies methods for the measurement of a.c. magnetic properties of materials in the frequency range 20 Hz to 200 kHz other than electrical steels and soft ferrites. The materials covered by this part of IEC 60404 include those speciality alloys listed in IEC 60404-8-6, amorphous and nanocrystalline materials, pressed and sintered and metal injection moulded parts such as are listed in IEC 60404-8-9, cast parts and magnetically soft composite materials. The object of this part is to define the general principles and the technical details of the measurement of the magnetic properties of magnetically soft materials by means of ring methods. For materials supplied in powder form, a ring test specimen is formed by the appropriate pressing method for that material. DC magnetic measurements on magnetically soft materials shall be made in accordance with the ring method of IEC 60404-4. The determinations of the magnetic characteristics of magnetically soft components shall be made in accordance with IEC 62044-3. Normally, the measurements shall be made at an ambient temperature of (23 ± 5) °C on ring test specimens which have first been magnetized, then demagnetized. Measurements can be made over other temperature ranges by agreement between supplier and purchaser. The scope of the second edition has been extended to include all magnetically soft materials except ferrites. The contents of the corrigendum of February 2009 have been included in this copy.