BS EN ISO 15512:2019

This document specifies methods for the determination of the water content of plastics in the form of powder, granules, and finished articles.

1 This document specifies methods for the determination of the water content of plastics in the form of powder, granules, and finished articles. These methods do not test for water absorption (kinetics and equilibrium) of plastics as measured by ISO62.MethodA is suitable for the determination of water content as low as 0,1% with an accuracy of 0,1%. MethodB and MethodC are suitable for the determination of water content as low as 0,01% with an accuracy of 0,01%. MethodD is suitable for the determination of water content as low as 0,01% with an accuracy of 0,01%. MethodE is suitable for the determination of water content as low as 0,001% with an accuracy of 0,001%. The stated accuracies are detection limits which depend also on the maximal possible sample mass. The water content is expressed as a percentage mass fraction of water.MethodD is suitable for polyamide (PA), polycarbonate (PC), polypropylene (PP), polyethylene (PE), epoxy resin, polyethylene terephthalate (PET), polyester, polytetrafluoroethylene (PTFE), polyvinyl chloride (PVC), polylactide (PLA), polyamidimid (PAI), it is especially not recommended for samples which can release NH3. MethodsA, B, C and E are generally suitable for all types of plastic and moisture level.Water content is an important parameter for processing materials and is expected to remain below the level specified in the appropriate material standard.Six alternative methods are specified in this document. — Method A is an extraction method using anhydrous methanol followed by a Karl Fischer titration of the extracted water. It can be used for all plastics and is applicable to granules smaller than 4mm×4mm×3mm. The method can also be used for, e.g. prepolymer materials in the form of a powder that are insoluble in methanol. — Method B1 is a vaporization method using a tube oven. The water contained in the test portion is vaporized and carried to the titration cell by a dry air or nitrogen carrier gas, followed by a Karl Fischer titration or a coulometric determination by means of a moisture sensor of the collected water. It can be used for all plastics and is applicable to granules smaller than 4mm×4mm×3mm. — Method B2 is a vaporization method using a heated sample vial. The water contained in the test portion is vaporized and carried to the titration cell by a dry air or nitrogen carrier gas, followed by a Karl Fischer titration of the collected water. It can be used for all plastics and is applicable to granules smaller than 4mm×4mm×3mm. — Method C is a manometric method. The water content is determined from the increase in pressure, which results when the water is evaporated under a vacuum. This method is not applicable to plastic samples containing volatile compounds, other than water, in amounts contributing significantly to the vapour pressure at room temperature. Checks for the presence of large amounts of volatile compounds are to be carried out periodically, for example by gas chromatography. Such checks are particularly required for new types or grades of material. — Method D is a thermocoulometric method using a diphosphorus pentoxide (P 2O 5) cell for the detection of the vaporized water. The water contained in the test portion is vaporized and carried to the sensor cell by a dry air or nitrogen carrier gas, followed by a coulometric determination of the collected water. This method is not applicable to plastic samples containing volatile compounds, other than water, in amounts contributing significantly to the vapour pressure at room temperature. This is specially related to volatile components which can react with the acidic coating of the diphosphorus pentoxide sensor, e.g. ammonia or any kind of amines. Checks for the presence of large amounts of volatile compounds are to be carried out periodically. Such checks are particularly required for new types or grades of material. — Method E is a calcium hydride based method. The water content of a sample evaporates due to a combination of vacuum and heating. The evaporated water reacts with calcium hydride to molecular hydrogen and calcium hydroxide. The hydrogen causes an increase of pressure in the vacuum that is proportional to the evaporated water. Volatile components, that do not react with calcium hydride condensate in a cooling trap and do not affect the measurement.