ASTM D 3045 : 1992 : R1997
Superseded
A superseded Standard is one, which is fully replaced by another Standard, which is a new edition of the same Standard.
View Superseded by
Standard Practice for Heat Aging of Plastics Without Load
Hardcopy , PDF
03-11-2018
English
10-11-1997
CONTAINED IN VOL. 08.02, 2015 Describes the exposure conditions for testing the resistance of plastics to oxidation or other degradation when exposed solely to hot air for extended periods of time.
Committee |
D 20
|
DocumentType |
Standard Practice
|
Pages |
5
|
ProductNote |
Reconfirmed 1997 Reconfirmed 2016
|
PublisherName |
American Society for Testing and Materials
|
Status |
Superseded
|
SupersededBy |
1.1 This practice is intended to define the exposure conditions for testing the resistance of plastics to oxidation or other degradation when exposed solely to hot air for extended periods of time. Only the procedure for heat exposure is specified, not the test method or specimen. The effect of heat on any particular property may be determined by selection of the appropriate test method and specimen.
1.2 This practice should be used as a guide to compare thermal aging characteristics of materials as measured by the change in some property of interest. This practice recommends procedures for comparing the thermal aging characteristics of materials at a single temperature. Recommended procedures for determining the thermal aging characteristics of a material at a series of temperatures for the purpose of estimating time to a defined property change at some lower temperature are also described.
1.3 This practice does not predict thermal aging characteristics where interactions between stress, environment, temperature, and time control failure occurs.
1.4 This standard does not purport to address all of the safety problems, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.
Note-ISO-2578 is considered to be technically equivalent to this practice.ASTM D7444 : 2018 : REV A | Standard Practice for Heat and Humidity Aging of Oxidatively Degradable Plastics<br> |
ASTM D 5721 : 2008 : R2018 | Standard Practice for Air-Oven Aging of Polyolefin Geomembranes |
ASTM D 5592 : 1994 : R2018 | Standard Guide for Material Properties Needed in Engineering Design Using Plastics |
ASTM D 4434/D4434M : 2015 | Standard Specification for Poly(Vinyl Chloride) Sheet Roofing |
ASTM D 3105 : 2017 | Standard Index of Methods for Testing Elastomeric and Plastomeric Roofing and Waterproofing Materials |
ASTM D 5870 : 2016 | Standard Practice for Calculating Property Retention Index of Plastics |
ASTM G 114 : 2014 | Standard Practices for Evaluating the Age Resistance of Polymeric Materials Used in Oxygen Service |
ASTM C 1173 : 2018 | Standard Specification for Flexible Transition Couplings for Underground Piping Systems |
ASTM D 6754/D6754M : 2015 | Standard Specification for Ketone Ethylene Ester Based Sheet Roofing |
ASTM E 2785 : 2014 | Standard Test Method for Exposure of Firestop Materials to Severe Environmental Conditions |
ASTM E 2925 : 2017 | Standard Specification for Manufactured Polymeric Drainage and Ventilation Materials Used to Provide a Rainscreen Function |
ISO 505:2017 | Conveyor belts — Method for the determination of the tear propagation resistance of textile conveyor belts |
ISO 2578:1993 | Plastics Determination of time-temperature limits after prolonged exposure to heat |
ASTM D 1870 : 1991 | Practice for Elevated Temperature Aging Using a Tubular Oven (Withdrawn 1998) |
ASTM D 1894 : 2014 : REDLINE | Standard Test Method for Static and Kinetic Coefficients of Friction of Plastic Film and Sheeting |
ASTM D 618 : 2013 : REDLINE | Standard Practice for Conditioning Plastics for Testing |
ISO 7590:2009 | Steel cord conveyor belts Methods for the determination of total thickness and cover thickness |
ISO 282:1992 | Conveyor belts — Sampling |
ISO 7622-2:2015 | Steel cord conveyor belts Longitudinal traction test Part 2: Measurement of tensile strength |
ISO 8094:2013 | Steel cord conveyor belts — Adhesion strength test of the cover to the core layer |
ASTM D 1149 : 2016-02 | TEST METHODS FOR RUBBER DETERIORATION - CRACKING IN AN OZONE CONTROLLED ENVIRONMENT |
ISO 4649:2017 | Rubber, vulcanized or thermoplastic — Determination of abrasion resistance using a rotating cylindrical drum device |
ASTM D 3183 : 201 | PRACTICE FOR RUBBER - PREPARATION OF PIECES FOR TEST PURPOSES FROM PRODUCTS |
ISO 9856:2016 | Conveyor belts Determination of elastic and permanent elongation and calculation of elastic modulus |
ASTM D 413 : 1998 | Standard Test Methods for Rubber Property-Adhesion to Flexible Substrate |
ARPM IP1 : 2011 | CONVEYOR AND ELEVATOR BELT HANDBOOK |
ISO 7623:2015 | Steel cord conveyor belts — Cord-to-coating bond test — Initial test and after thermal treatment |
ISO 340:2013 | Conveyor belts Laboratory scale flammability characteristics Requirements and test method |
ISO 283:2015 | Textile conveyor belts — Full thickness tensile strength, elongation at break and elongation at the reference load — Test method |
ISO 284:2012 | Conveyor belts — Electrical conductivity — Specification and test method |
ASTM D 865 : 2011 | Standard Test Method for Rubber<char: emdash>Deterioration by Heating in Air (Test Tube Enclosure) |
CFR 30(PTS1-199) : JUL 2017 | MINERAL RESOURCES - MINE SAFETY & HEALTH ADMINISTRATION, DEPARTMENT OF LABOUR |
ISO 7622-1:2013 | Steel cord conveyor belts — Longitudinal traction test — Part 1: Measurement of elongation |
ASTM D 4483 : 2014-02 | PRACTICE FOR EVALUATING PRECISION FOR TEST METHOD STANDARDS IN THE RUBBER AND CARBON BLACK MANUFACTURING INDUSTRIES |
ASTM D 471 : 2016-02 | TEST METHOD FOR RUBBER PROPERTY - EFFECT OF LIQUIDS |
Access your standards online with a subscription
Features
-
Simple online access to standards, technical information and regulations.
-
Critical updates of standards and customisable alerts and notifications.
-
Multi-user online standards collection: secure, flexible and cost effective.