BIS IS 1608 : 2005
Withdrawn
A Withdrawn Standard is one, which is removed from sale, and its unique number can no longer be used. The Standard can be withdrawn and not replaced, or it can be withdrawn and replaced by a Standard with a different number.
View Superseded by
METALLIC MATERIALS - TENSILE TESTING AT AMBIENT TEMPERATURE
23-07-2013
12-01-2013
NATIONAL FOREWORD
1 Scope
2 Normative references
3 Principle
4 Definitions
5 Symbols and designations
6 Test piece
7 Determination of original cross-sectional
area (S[0])
8 Making the original gauge length (L[0])
9 Accuracy of testing apparatus
10 Conditions of testing
11 Determination of percentage elongation after
fracture (A)
12 Determination of percentage total elongation
at maximum force (A[gt])
13 Determination of proof strength, non proportional
extension (R[p])
14 Determination of proof strength, total extension (R[t])
15 Method of verification of permanent set strength (R[r])
16 Determination of percentage reduction of area (Z)
17 Accuracy of the results
18 Test report
Annex A (normative) - Types of test piece to be used
for thin products: sheets, strips and flats
between 0,1 mm and 3 mm thick
Annex B (normative) - Types of test piece to be used for wire,
bars and sections with a diameter or thickness of
less than 4 mm
Annex C (normative) - Types of test piece to be used for sheets
and flats of thickness equal to or greater than 3 mm,
and wire, bars and sections of diameter or thickness
equal to or greater than 4 mm
Annex D (normative) - Types of test piece to be used for tubes
Annex E (informative) - Precautions to be taken when measuring
the percentage elongation after fracture if the
specified value is less than 5%
Annex F (informative) - Nomogram for calculating the gauge
lengths of test pieces of rectangular cross-section
Annex G (informative) - Measurement of percentage elongation
after fracture based on subdivision of the original
gauge length
Annex H (informative) - Manual method of determination of
percentage total elongation at maximum force for
long products such as bars, wire, rods
Annex J (informative) - An "Error Budget" approach to the
estimation of the uncertainty of measurement in
tensile testing
Annex K (informative) - Precision of tensile testing - Results
from interlaboratory test programmes
Annex L (informative) - Bibliography
Describes the method for tensile testing of metallic materials and defines the mechanical properties which can be determined at ambient temperature.
Committee |
MTD 3
|
DevelopmentNote |
Supersedes BIS IS 8285, BIS IS 4713, BIS IS 2078, BIS IS 2654 BIS IS 2655, BIS IS 2656, BIS IS 2657, BIS IS 1521, BIS IS 1663, BIS IS 2658, BIS IS 1816 and BIS IS 1894. (09/2008) Also numbered as ISO 6892. (05/2009)
|
DocumentType |
Standard
|
PublisherName |
Bureau of Indian Standards
|
Status |
Withdrawn
|
SupersededBy | |
Supersedes |
BIS IS 11999 : 2007(R2009) | METHOD FOR DETERMINATION OF PLASTIC STRAIN RATIO 'R' FOR STEEL SHEETS |
BIS IS 1865 : 1991(R2005) | IRON CASTINGS WITH SPHEROIDAL OR NODULAR GRAPHITE - SPECIFICATION |
BIS IS 2148 : 2004 AMD 2 2008 | ELECTRICAL APPARATUS FOR EXPLOSIVE GAS ATMOSPHERES - FLAMEPROOF ENCLOSURES "D" |
BIS IS 3224 : 2002 AMD 3 2014 | VALVE FITTINGS FOR COMPRESSED GAS CYLINDERS EXCLUDING LIQUEFIED PETROLEUM GAS (LPG) CYLINDERS - SPECIFICATION |
BIS IS 8800 : 1997 AMD 1 2009 | TECHNICAL DELIVERY CONDITIONS FOR STEEL CASTINGS (EXCLUDING INVESTMENT CASTINGS) |
BIS IS 15834 : 2008 AMD 1 2013 | STAINLESS STEEL SLIDING DOOR BOLTS USE WITH PADLOCKS - SPECIFICATION |
BIS IS 6527 : 1995(R2014) | STAINLESS STEEL WIRE RODS - SPECIFICATION |
BIS IS 3589 : 2001 AMD 4 2010 | STEEL PIPES FOR WATER AND SEWAGE (168.3 TO 2540 MM OUTSIDE DIAMETER) - SPECIFICATION |
BIS IS 7285-2 : 2017 | REFILLABLE SEAMLESS STEEL GAS CYLINDERS - SPECIFICATION - PART 2: QUENCHED AND TEMPERED STEEL CYLINDERS WITH TENSILE STRENGTH LESS THAN 1100 MPA (112 KGF/MM[2]) |
BIS IS 6911 : 2017 AMD 1 2017 | STAINLESS STEEL PLATE, SHEET AND STRIP - SPECIFICATION |
BIS IS 15977 : 2013 | CLASSIFICATION AND ACCEPTANCE TESTS FOR BARE SOLID WIRE ELECTRODES AND WIRE FLUX COMBINATION FOR SUBMERGED ARC WELDING OF STRUCTRUAL STEEL - SPECIFICATION |
BIS IS 14899 : 2014 | LIQUEFIED PETROLEUM GAS (LPG) CONTAINERS FOR AUTOMOTIVE USE - SPECIFICATION |
BIS IS 1161 : 2014 | STEEL TUBES FOR STRUCTURAL PURPOSES - SPECIFICATION |
BIS IS 6006 : 2014 | UNCOATED STRESS RELIEVED STRAND FOR PRESTRESSED CONCRETE - SPECIFICATION |
BIS IS 5082 : 1998(R2003) | WROUGHT ALUMINIUM AND ALUMINIUM ALLOY BARS, RODS, TUBES, SECTIONS, PLATES AND SHEETS FOR ELECTRICAL APPLICATIONS |
BIS IS 6240 : 2008 | HOT ROLLED STEEL PLATE (UP TO 6 MM) SHEET AND STRIP FOR THE MANUFACTURE OF LOW PRESSURE LIQUEFIABLE GAS CYLINDERS |
BIS IS 1285 : 2002(R2012) | WROUGHT ALUMINIUM AND ALUMINIUM ALLOYS - EXTRUDED ROUND TUBE AND HOLLOW SECTIONS FOR GENERAL ENGINEERING PURPOSES - SPECIFICATION |
BIS IS 2004 : 1991(R2012) | CARBON STEEL FORGINGS FOR GENERAL ENGINEERING PURPOSES - SPECIFICATION |
BIS IS 16172 : 2014 | REINFORCEMENT COUPLERS FOR MECHANICAL SPLICES OF BARS IN CONCRETE - SPECIFICATION |
BIS IS 2041 : 2009(R2013) | STEEL PLATES FOR PRESSURE VESSELS USED AT MODERATE AND LOW TEMPERATURE - SPECIFICATION |
BIS IS 6912 : 2005(R2016) | COPPER AND COPPER ALLOY FORGING STOCK AND FORGING - SPECIFICATION |
BIS IS 14698 : 1999(R2012) | CARBON AND LOW ALLOY STEEL BILLETS, BLOOMS, SLABS AND BARS FOR MANUFACTURE OF SHELL BODIES AND PROOF SHOTS USED IN DEFENCE SERVICES - SPECIFICATION |
BIS IS 280 : 2006(R2015) | MILD STEEL WIRE FOR GENERAL ENGINEERING PURPOSES |
BIS IS 4454-1 : 2001(R2015) | STEEL WIRE FOR MECHANICAL SPRINGS - SPECIFICATION - PART 1: COLD DRAWN UNALLOYED STEEL WIRE |
BIS IS 319 : 2007 | FREE CUTTING BRASS BARS, RODS AND SECTION - SPECIFICATION |
BIS IS 3074 : 2013 | STEEL TUBES FOR AUTOMOTIVE PURPOSES - SPECIFICATION |
BIS IS 613 : 2000(R2016) | COPPER RODS AND BARS FOR ELECTRICAL PURPOSES - SPECIFICATION |
BIS IS 15769 : 2008 | FLUX CORED (TUBULAR) ELECTRODES FOR GAS SHIELDED AND SELF-SHIELDED METAL WELDING OF CARBON OR CARBON-MANGANESE STEEL |
BIS IS 814 : 2004(R2010) | COVERED ELECTRODES FOR MANUAL METAL ARC WELDING OF CARBON AND CARBON MANGANESE STEEL - SPECIFICATION |
BIS IS 2062 : 2011(R2016) | HOT ROLLED MEDIUM AND HIGH TENSILE STRUCTURAL STEEL - SPECIFICATION |
BIS IS 1239-2 : 2011 AMD 1 2012 | STEEL TUBES, TUBULARS AND OTHER STEEL FITTINGS - SPECIFICATION - PART 2: STEEL PIPE FITTINGS |
BIS IS 4896 : 1992(R2002) | ONE-PERCENT CHROMIUM STEEL CASTINGS FOR RESISTANCE TO ABRASION - SPECIFICATION |
BIS IS 4454-2 : 2001(R2015) | STEEL WIRES FOR MECHANICAL SPRINGS - SPECIFICATION - PART 2: OIL HARDENED AND TEMPERED STEEL WIRE |
BIS IS 800 : 2007 AMD 1 2012 | GENERAL CONSTRUCTION IN STEEL - CODE OF PRACTICE |
BIS IS 4454-4 : 2001(R2005) | STEEL WIRES FOR MECHANICAL SPRINGS - SPECIFICATION - PART 4: STAINLESS STEEL WIRE |
BIS IS 1993 : 2006 AMD 1 2010 | COLD-REDUCED ELECTROLYTIC TINPLATE |
BIS IS 513 : 2008 AMD 2 2016 | COLD REDUCED LOW CARBON STEEL SHEET AND STRIP |
BIS IS 4692 : 2013 | SHIPBUILDING - ELECTRICALLY WELDED STUDLESS LINK ANCHOR CHAINS AND CONNECTING SHACKLES - SPECIFICATION |
BIS IS 2002 : 2009 AMD 1 2012 | STEEL PLATE FOR PRESSURE VESSEL FOR INTERMEDIATE AND HIGH TEMPERATURE SERVICE INCLUDING BOILERS |
BIS IS 3038 : 2006 | MARTENSITIC STAINLESS STEEL AND ALLOY STEEL CASTINGS FOR PRESSURE CONTAINING PARTS SUITABLE FOR HIGH TEMPERATURE SERVICE - SPECIFICATION |
BIS IS 3930 : 1994(R2014) | FLAME AND INDUCTION HARDENING STEELS - SPECIFICATION |
BIS IS/ISO 3183 : 2007 | PETROLEUM AND NATURAL GAS INDUSTRIES - STEEL PIPE FOR PIPELINE TRANSPORTATION SYSTEMS |
BIS IS 1239-1 : 2004 AMD 5 2017 | STEEL TUBES, TUBULARS AND OTHER WROUGHT STEEL FITTINGS - SPECIFICATION - PART 1: STEEL TUBES |
BIS IS 13352 : 1992(R2009) | STOCK FOR FORGINGS PRODUCED FROM CONTINUOUSLY CAST BLOOMS, BILLETS AND SLABS - SPECIFICATION |
BIS IS 4484 : 2013 | SHIPBUILDING - ELECTRICALLY WELDED STUD LINK ANCHOR CHAINS AND CONNECTING SHACKLES AND SWIVELS - SPECIFICATION |
BIS IS 2707 : 1996(R2002) | CARBON STEEL CASTINGS FOR SURFACE HARDENING - SPECIFICATION |
BIS IS 4270 : 2001 AMD 2 2017 | STEEL TUBES USED FOR WATER WELLS - SPECIFICATION |
BIS IS 3601 : 2006 AMD 1 2012 | STEEL TUBES FOR MECHANICAL AND GENERAL ENGINEERING PURPOSES - SPECIFICATION |
BIS IS 1180-1 : 2014 AMD 2 2017 | OUTDOOR TYPE OIL IMMERSED DISTRIBUTION TRANSFORMERS UPTO AND INCLUDING 2500 KVA, 33KV - SPECIFICATION - PART 1: MINERAL OIL IMMERSED |
BIS IS 5517 : 1993(R2014) | STEELS FOR HARDENING AND TEMPERING - SPECIFICATION |
BIS IS 737 : 2008(R2013) | WROUGHT ALUMINIUM AND ALUMINIUM ALLOY SHEET AND STRIP FOR GENERAL ENGINEERING PURPOSES - SPECIFICATION |
BIS IS 1030 : 1998 | CARBON STEEL CASTINGS FOR GENERAL ENGINEERING PURPOSES - SPECIFICATION |
BIS IS 15961 : 2012 AMD 1 2016 | HOT DIP ALUMINIUM-ZINC ALLOY METALLIC COATED STEEL STRIP AND SHEET (PLAIN) |
BIS IS 1990 : 2009 | STEEL RIVET AND STAY BARS FOR BOILERS |
BIS IS 15935 : 2011 AMD 1 2013 | COMPOSITE CYLINDERS FOR ON-BOARD STORAGE OF COMPRESSED NATURAL GAS (CNG) AS A FUEL FOR AUTOMOTIVE VEHICLE - SPECIFICATION |
BIS IS 8329 : 2000 AMD 3 2014 | CENTRIFUGALLY CAST (SPUN) DUCTILE IRON PRESSURE PIPES FOR WATER, GAS AND SEWAGE - SPECIFICATION |
BIS IS 15997 : 2012 | LOW NICKEL AUSTENITIC STAINLESS STEEL SHEET AND STRIP FOR UTENSILS AND KITCHEN APPLIANCES - SPECIFICATION |
BIS IS 14491 : 1997(R2007) | LOW CARBON HIGH STRENGTH COLD ROLLED STEEL SHEETS AND COILS FOR COLD FORMING - SPECIFICATION |
BIS IS 1996 : 2003 | LABORATORY GLASSWARE - STRAIGHT-BORE GLASS STOPCOCKS FOR GENERAL PURPOSES |
BIS IS 1786 : 2008 AMD 3 2017 | HIGH STRENGTH DEFORMED STEEL BARS AND WIRES FOR CONCRETE REINFORCEMENT - SPECIFICATION |
BIS IS 210 : 2009(R2014) | GREY IRON CASTINGS - SPECIFICATION |
ISO/IEC Guide 98:1993 | Guide to the expression of uncertainty in measurement (GUM) |
BIS IS 3803-2 : 1989(R2006) | STEEL - CONVERSION OF ELONGATION VALUES - PART 2: AUSTENITIC STEELS |
ISO 2566-2:1984 | Steel Conversion of elongation values Part 2: Austenitic steels |
BIS IS 3803-1 : 1989(R2010) | STEEL - CONVERSION OF ELONGATION VALUES - PART 1: CARBON AND LOW ALLOY STEELS |
ISO 9513:2012 | Metallic materials — Calibration of extensometer systems used in uniaxial testing |
BIS IS 1828-1 : 2015 | METALLIC MATERIALS - VERIFICATION OF STATIC UNIAXIAL TESTING MACHINES - PART 1: TENSION/COMPRESSION TESTING MACHINES - VERIFICATION AND CALIBRATION OF THE FORCE-MEASURING SYSTEM |
ISO 2566-1:1984 | Steel Conversion of elongation values Part 1: Carbon and low alloy steels |
BIS IS 12872 : 2011 | METALLIC MATERIALS - CALIBRATION OF EXTENSOMETERS USED IN UNIAXIAL TESTING |
ISO 5725-2:1994 | Accuracy (trueness and precision) of measurement methods and results Part 2: Basic method for the determination of repeatability and reproducibility of a standard measurement method |
ISO 286-2:2010 | Geometrical product specifications (GPS) ISO code system for tolerances on linear sizes Part 2: Tables of standard tolerance classes and limit deviations for holes and shafts |
ISO 7500-1:2015 | Metallic materials Calibration and verification of static uniaxial testing machines Part 1: Tension/compression testing machines Calibration and verification of the force-measuring system |
BIS IS 919-2 : 2014 | GEOMETRICAL PRODUCT SPECIFICATIONS (GPS) - ISO CODE SYSTEM FOR TOLERANCES ON LINEAR SIZES - PART 2: TABLES OF STANDARD TOLERANCE CLASSES AND LIMIT DEVIATION FOR HOLES SHAFTS |
BIS IS 3711 : 2012 | STEEL AND STEEL PRODUCTS - LOCATION AND PREPARATION OF SAMPLES AND TEST PIECES FOR MECHANICAL TESTING |
ISO 377:2017 | Steel and steel products — Location and preparation of samples and test pieces for mechanical testing |
Access your standards online with a subscription
Features
-
Simple online access to standards, technical information and regulations.
-
Critical updates of standards and customisable alerts and notifications.
-
Multi-user online standards collection: secure, flexible and cost effective.