ISO 16539:2013
Current
The latest, up-to-date edition.
Corrosion of metals and alloys — Accelerated cyclic corrosion tests with exposure to synthetic ocean water salt-deposition process — "Dry" and "wet" conditions at constant absolute humidity
Hardcopy , PDF , PDF 3 Users , PDF 5 Users , PDF 9 Users
French, English
14-02-2013
Important note : Users cannot be edited or removed once added to your Multi user PDF.
This International Standard specifies two accelerated corrosion test procedures, Methods A and B, for the evaluation of corrosion behaviour of surface-treated metals and their alloys with and without paint on them in atmospheric environments. It also specifies the apparatus used. The two tests involve salt deposition and dry/wet conditions at a constant absolute humidity.
Method A applies to:
metals and their alloys (including corrosion-resistance alloys)
Method B applies to:
metals and their alloys
metals and their alloys with coatings [including metallic coatings (anodic or cathodic), organic
coatings, and conversion coatings]
| DevelopmentNote |
Supersedes ISO/DIS 16539. (02/2013)
|
| DocumentType |
Standard
|
| Pages |
19
|
| PublisherName |
International Organization for Standardization
|
| Status |
Current
|
| Standards | Relationship |
| BS ISO 16539:2013 | Identical |
| NF EN ISO 16539:2022 | Identical |
| ÖNORM EN ISO 16539:2022 09 15 | Identical |
| UNI EN ISO 16539:2022 | Identical |
| SN EN ISO 16539:2022 | Identical |
| NS-EN ISO 16539:2022 | Identical |
| PN-EN ISO 16539:2022-12 | Identical |
| UNE-EN ISO 16539:2023 | Identical |
| BS EN ISO 16539:2022 | Identical |
| ISO 9223:2012 | Corrosion of metals and alloys — Corrosivity of atmospheres — Classification, determination and estimation |
| ISO 8993:2010 | Anodizing of aluminium and its alloys Rating system for the evaluation of pitting corrosion Chart method |
| ISO 11130:2010 | Corrosion of metals and alloys Alternate immersion test in salt solution |
| ISO 3574:2012 | Cold-reduced carbon steel sheet of commercial and drawing qualities |
| ISO 14993:2001 | Corrosion of metals and alloys Accelerated testing involving cyclic exposure to salt mist, "dry" and "wet" conditions |
| ISO 4628-4:2016 | Paints and varnishes Evaluation of degradation of coatings Designation of quantity and size of defects, and of intensity of uniform changes in appearance Part 4: Assessment of degree of cracking |
| ISO 4628-3:2016 | Paints and varnishes — Evaluation of degradation of coatings — Designation of quantity and size of defects, and of intensity of uniform changes in appearance — Part 3: Assessment of degree of rusting |
| ISO 17872:2007 | Paints and varnishes Guidelines for the introduction of scribe marks through coatings on metallic panels for corrosion testing |
| ISO 4628-5:2016 | Paints and varnishes — Evaluation of degradation of coatings — Designation of quantity and size of defects, and of intensity of uniform changes in appearance — Part 5: Assessment of degree of flaking |
| ISO 4628-1:2016 | Paints and varnishes Evaluation of degradation of coatings Designation of quantity and size of defects, and of intensity of uniform changes in appearance Part 1: General introduction and designation system |
| ISO 9227:2017 | Corrosion tests in artificial atmospheres — Salt spray tests |
| ISO 8407:2009 | Corrosion of metals and alloys Removal of corrosion products from corrosion test specimens |
| ISO 10289:1999 | Methods for corrosion testing of metallic and other inorganic coatings on metallic substrates Rating of test specimens and manufactured articles subjected to corrosion tests |
| ISO 4628-2:2016 | Paints and varnishes Evaluation of degradation of coatings Designation of quantity and size of defects, and of intensity of uniform changes in appearance Part 2: Assessment of degree of blistering |
Access your standards online with a subscription
Features
-
Simple online access to standards, technical information and regulations.
-
Critical updates of standards and customisable alerts and notifications.
-
Multi-user online standards collection: secure, flexible and cost effective.