TS220 Technical Specification for Self Locking Union Nuts (Unified Threads) Manufactured from INCO718 Material.1270 MPa (185000 lbf/in2) Minimum Tensile Strength at Room Temperature
Hardcopy , PDF
07-11-2022
English
01-02-2005
Important note : Users cannot be edited or removed once added to your Multi user PDF.
1. Scope
2. Requirements
3. Normative References
4. Definitions
5. Quality Assurance
6. Test Equipment
7. Technical Requirements & Test Methods
8. Thrust Wire Seating Bedding-In Process
APPENDIX A - Permanent Set Test
APPENDIX B - Dimension & Material of Test Pieces
for Reusability Test
APPENDIX C - Thrust Wire
Determines the requirements and the appropriate performance, inspection and production acceptance tests which apply to self-locking Union Nuts. Covers the procedures to be followed by a manufacturer to become qualified to supply self-locking Union Nuts to this specification.
| DevelopmentNote |
Amendment Record is available separately, see SBAC TS 220 AR. (05/2017)
|
| DocumentType |
Standard
|
| Pages |
25
|
| PublisherName |
SAE Industry Technologies Consortia
|
| Status |
Superseded
|
| SupersededBy |
| ISO 6507-1:2005 | Metallic materials Vickers hardness test Part 1: Test method |
| BS 7S 80:2002 | High chromium-nickel corrosion resisting steel forging stock, bars, forgings and parts (880 to 1080 MPa: limiting ruling section 100 mm) |
| SAE AMS 5663 : 2016 | NICKEL ALLOY, CORROSION AND HEAT-RESISTANT, BARS, FORGINGS, AND RINGS 52.5NI - 19CR - 3.0MO - 5.1CB (NB) - 0.90TI - 0.50AL - 18FE CONSUMABLE ELECTRODE OR VACUUM INDUCTION MELTED 1775 DEGREES F (968 DEGREES C) SOLUTION AND PRECIPITATION HEAT TREATED |
| SAE AMS 5628 : 2015 | STEEL, CORROSION-RESISTANT, BARS, WIRE, FORGINGS, AND TUBING, 16CR - 2.5NI (SAE 51431) |
| ISO 6506-1:2014 | Metallic materials Brinell hardness test Part 1: Test method |
| BS A 346:2000 | UNJ threads. General requirements and limit dimensions |
| ISO 6508-1:2016 | Metallic materials — Rockwell hardness test — Part 1: Test method |
| DEFSTAN 91-98/2(2001) : 2001 | LUBRICATING OIL, GAS TURBINE ENGINE, SYNTHETIC GRADE 7.5 CST NATO CODE: O-149 JOINT SERVICE DESIGNATION: OX-38 |
| BS 6001-1(1999) : 1999 | SAMPLING PROCEDURES FOR INSPECTION BY ATTRIBUTES - PART 1: SAMPLING SCHEMES INDEXED BY ACCEPTANCE QUALITY LIMIT (AQL) FOR LOT-BY-LOT INSPECTION |
| ASME B46.1 : 2009 | SURFACE TEXTURE (SURFACE ROUGHNESS, WAVINESS, AND LAY) |
| ISO 3452-1:2013 | Non-destructive testing Penetrant testing Part 1: General principles |
| BS 2S 130:1976 | Specification for 18/9 chromium-nickel corrosion-resisting steel (niobium stabilized) billets, bars, forgings and parts (540 MPa: limiting ruling section 150 mm) |
| BS 1580-1:2007 | Unified screw threads Screw threads with diameters ¼ in and larger. Requirements |
| SAE AS 8879 : 2004 | SCREW THREADS - UNJ PROFILE, INCH CONTROLLED RADIUS ROOT WITH INCREASED MINOR DIAMETER |
| ISO 9001:2015 | Quality management systems — Requirements |
| ASTM A 276/A276M : 2017 : REDLINE | Standard Specification for Stainless Steel Bars and Shapes |
| SAEITC TS46-3 | TS46 Assembly of Union Nuts, Thrust Wires and Union Ferrules |
| ISO 3161:1999 | Aerospace — UNJ threads — General requirements and limit dimensions |
Access your standards online with a subscription
Features
-
Simple online access to standards, technical information and regulations.
-
Critical updates of standards and customisable alerts and notifications.
-
Multi-user online standards collection: secure, flexible and cost effective.