EN 10292:2007

Foreword
1 Scope
2 Normative references
3 Terms and definitions
4 Classification and designation
   4.1 Classification
   4.2 Designation
5 Information to be supplied by the purchaser
   5.1 Mandatory information
   5.2 Options
6 Manufacturing process
7 Requirements
   7.1 Chemical composition
   7.2 Mechanical properties
   7.3 Requirements for coatings
   7.4 Tolerances on dimensions and shape
   7.5 Suitability for further processing
8 Testing
   8.1 General
   8.2 Test units
   8.3 Number of tests
   8.4 Sampling
   8.5 Test methods
   8.6 Retests
   8.7 Inspection documents
9 Marking
10 Packing
11 Storage and transportation
12 Disputes
Annex A (normative) Reference method for
        determination of the zinc, zinc-iron,
        zinc-aluminium and aluminium-zinc
        coating mass
Annex B (normative) Reference method for
        determination of the aluminium-silicon
        coating mass
Annex C (normative) Methods for determination of
        the mass of the Fe-Al-Si alloy layer
Bibliography

This European Standard specifies requirements for continuously hot-dip zinc (Z), zinc-iron alloy (ZF), zinc-aluminium alloy (ZA), aluminium-zinc alloy (AZ) and aluminium-silicon alloy (AS) coated flat products made of steels with high yield strength for cold forming (see Tables 1 and 3) with thicknesses up to and including

3,0 mm unless otherwise agreed. The thickness is the final thickness of the delivered product after coating.

This European Standard applies to strip of all widths and to sheets cut from it ( 600 mm width) and cut lengths (< 600 mm width).

The products covered by this European Standard are mainly used where cold formability and corrosion resistance for a defined minimum yield strength are the most important factors.