EN ISO 9015-1:2011
Current
The latest, up-to-date edition.
Destructive tests on welds in metallic materials - Hardness testing - Part 1: Hardness test on arc welded joints (ISO 9015-1:2001)
02-03-2011
Foreword
1 Scope
2 Normative references
3 Principle
4 Symbols and terms
5 Preparation of test specimens
6 Test procedure
7 Test results
8 Test report
Annex A (informative) - Example of a test report for
hardness testing (R) on welded joints
Annex B (informative) - Example of a test report for
hardness testing (E) on welded joints
This part of ISO 9015 specifies hardness tests on transverse sections of arc welded joints of metallic materials. Itcovers Vickers hardness tests in accordance with ISO 6507-1, normally with test loads of 49,03 N or 98,07 N (HV 5or HV 10).However, the principles may be applied to Brinell hardness testing (with appropriate testing loads of HB 2,5/15,625or HB 1/2,5) in accordance with ISO 6506-1 and micro hardness testing in accordance with ISO 6507-1 andISO 9015-2.NOTE Testing should be carried out to ensure that the highest and the lowest level of hardness of both parent metal andweld metal is determined.This part of ISO 9015 does not apply to test welds in austenitic stainless steels.
| Committee |
CEN/TC 121
|
| DevelopmentNote |
Supersedes EN 1043-1. (03/2011)
|
| DocumentType |
Standard
|
| PublisherName |
Comite Europeen de Normalisation
|
| Status |
Current
|
Access your standards online with a subscription
Features
-
Simple online access to standards, technical information and regulations.
-
Critical updates of standards and customisable alerts and notifications.
-
Multi-user online standards collection: secure, flexible and cost effective.