BS ISO 17804:2005
Superseded
A superseded Standard is one, which is fully replaced by another Standard, which is a new edition of the same Standard.
View Superseded by
Founding. Ausferritic spheroidal graphite ausferrite cast iron. Classification
Hardcopy , PDF
09-06-2020
English
25-01-2006
Foreword
Introduction
1 Scope
2 Normative references
3 Terms and definitions
4 Designation
5 Order information
6 Manufacture
7 Requirements
7.1 General
7.2 Test pieces machined from separately cast and cast-on
samples
7.3 Test pieces machined from samples cut from a casting
7.4 Hardness
7.5 Graphite structure
7.6 Matrix structure
8 Sampling
8.1 General
8.2 Separately cast samples
8.3 Cast-on samples
8.4 Samples cut from a casting
9 Test methods
9.1 Tensile test
9.2 Impact test, Charpy V
9.3 Hardness test
10 Retests
10.1 Need for retesting
10.2 Test validity
10.3 Non-conforming test results
10.4 Heat treatment of samples and castings
11 Additional information
Annex A (normative) - Abrasion-resistant grades of ausferritic
spheroidal graphite cast iron
Annex B (normative) - Minimum elongation values for a test
piece with original gauge length L[0] = 4 x d
Annex C (informative) - Guidance values for Brinell hardness
Annex D (informative) - Procedure for the determination of
the hardness range
Annex E (informative) - Guidance values for tensile strength
and elongation for test pieces machined from
samples cut from a casting [1]
Annex F (informative) - Unnotched impact test
Annex G (informative) - Additional information on mechanical
and physical properties
Annex H (informative) - Nodularity (or spheroidal graphite
rate)
Annex I (informative) - Machinability of ausferritic spheroidal
graphite cast irons
Annex J (informative) - Cross-references of similar grades of
ausferritic spheroidal graphite cast iron
Bibliography
Specifies the grades and the corresponding requirements for ausferritic spheroidal graphite cast irons. Defines five grades of ausferritic spheroidal graphite cast iron by a classification based on mechanical properties measured on machined test pieces prepared from separately cast samples or cast-on samples, and samples cut from a casting. Also specifies two grades by a classification as a function of hardness.
Committee |
ISE/111
|
DevelopmentNote |
Supersedes 03/118501 DC. (02/2006)
|
DocumentType |
Standard
|
Pages |
40
|
PublisherName |
British Standards Institution
|
Status |
Superseded
|
SupersededBy | |
Supersedes |
Standards | Relationship |
ISO 17804:2005 | Identical |
ISO 6507-1:2005 | Metallic materials Vickers hardness test Part 1: Test method |
ISO 6506-1:2014 | Metallic materials Brinell hardness test Part 1: Test method |
ISO 148-2:2016 | Metallic materials — Charpy pendulum impact test — Part 2: Verification of testing machines |
ISO 1083:2004 | Spheroidal graphite cast irons - Classification |
ASTM A 897/A897M : 2016 : REDLINE | Standard Specification for Austempered Ductile Iron Castings |
ISO 6892:1998 | Metallic materials Tensile testing at ambient temperature |
ISO 148-1:2016 | Metallic materials — Charpy pendulum impact test — Part 1: Test method |
ISO 6336-5:2016 | Calculation of load capacity of spur and helical gears Part 5: Strength and quality of materials |
ISO 148-3:2016 | Metallic materials — Charpy pendulum impact test — Part 3: Preparation and characterization of Charpy V-notch test pieces for indirect verification of pendulum impact machines |
SAE J 2477 : 2004 | AUTOMOTIVE AUSTEMPERED DUCTILE (NODULAR) IRON CASTINGS (ADI) |
ISO/TR 15931:2004 | Designation system for cast irons and pig irons |
ISO 945:1975 | Cast iron — Designation of microstructure of graphite |
Access your standards online with a subscription
Features
-
Simple online access to standards, technical information and regulations.
-
Critical updates of standards and customisable alerts and notifications.
-
Multi-user online standards collection: secure, flexible and cost effective.