Destructive tests on welds in metallic materials Hardness testing Part 1: Hardness test on arc welded joints
Hardcopy , PDF , PDF 3 Users , PDF 5 Users , PDF 9 Users
English, French
29-03-2001
This part of ISO 9015 specifies hardness tests on transverse sections of arc welded joints of metallic materials. It
covers Vickers hardness tests in accordance with ISO 6507-1, normally with test loads of 49,03 N or 98,07 N (HV 5
or HV 10).
However, the principles may be applied to Brinell hardness testing (with appropriate testing loads of HB 2,5/15,625
or HB 1/2,5) in accordance with ISO 6506-1 and micro hardness testing in accordance with ISO 6507-1 and
ISO 9015-2.
NOTE Testing should be carried out to ensure that the highest and the lowest level of hardness of both parent metal and
weld metal is determined.
This part of ISO 9015 does not apply to test welds in austenitic stainless steels.
DocumentType |
Standard
|
Pages |
14
|
PublisherName |
International Organization for Standardization
|
Status |
Current
|
Standards | Relationship |
NF EN ISO 9015-1 : 2011 | Identical |
NBN EN ISO 9015-1 : 2011 | Identical |
NEN EN ISO 9015-1 : 2011 | Identical |
NS EN ISO 9015-1 : 2011 | Identical |
I.S. EN ISO 9015-1:2011 | Identical |
PN EN ISO 9015-1 : 2011 | Identical |
SN EN ISO 9015-1 : 2011 | Identical |
UNI EN ISO 9015-1 : 2011 | Identical |
SS-EN ISO 9015-1:2011 | Identical |
UNE-EN ISO 9015-1:2011 | Identical |
BS EN ISO 9015-1:2011 | Identical |
EN ISO 9015-1:2011 | Identical |
DIN EN ISO 9015-1:2011-05 | Identical |
14/30266380 DC : 0 | BS EN ISO 15614-8 - SPECIFICATION AND QUALIFICATION OF WELDING PROCEDURES FOR METALLIC MATERIALS - WELDING PROCEDURE TEST - PART 8: WELDING OF TUBES TO TUBE-PLATE JOINTS |
DIN ISO 22826:2008-08 | Destructive tests on welds in metallic materials - Hardness testing of narrow joints welded by laser and electron beam (Vickers and Knoop hardness tests) (ISO 22826:2005) |
DIN EN ISO 9015-2:2016-10 | DESTRUCTIVE TESTS ON WELDS IN METALLIC MATERIALS - HARDNESS TESTING - PART 2: MICROHARDNESS TESTING OF WELDED JOINTS (ISO 9015-2:2016) |
DIN EN ISO 15614-14:2013-12 | SPECIFICATION AND QUALIFICATION OF WELDING PROCEDURES FOR METALLIC MATERIALS - WELDING PROCEDURE TEST - PART 14: LASER-ARC HYBRID WELDING OF STEELS, NICKEL AND NICKEL ALLOYS (ISO 15614-14:2013) |
I.S. EN ISO 15614-7:2016 | SPECIFICATION AND QUALIFICATION OF WELDING PROCEDURES FOR METALLIC MATERIALS - WELDING PROCEDURE TEST - PART 7: OVERLAY WELDING |
11/30235519 DC : 0 | BS EN ISO 15614-14 - SPECIFICATION AND QUALIFICATION OF WELDING PROCEDURES FOR METALLIC MATERIALS - WELDING PROCEDURE TEST - PART 14: LASER-ARC HYBRID WELDING OF STEELS, NICKEL AND NICKEL ALLOYS |
PREN ISO 15614-13 : DRAFT 2010 | SPECIFICATION AND QUALIFICATION OF WELDING PROCEDURES FOR METALLIC MATERIALS - WELDING PROCEDURE TEST - PART 13: RESISTANCE BUTT (UPSET) AND FLASH WELDING |
ISO 22826:2005 | Destructive tests on welds in metallic materials — Hardness testing of narrow joints welded by laser and electron beam (Vickers and Knoop hardness tests) |
I.S. EN 13445-4:2014 | UNFIRED PRESSURE VESSELS - PART 4: FABRICATION |
EN ISO 15614-13:2012 | Specification and qualification of welding procedures for metallic materials - Welding procedure test - Part 13: Upset (resistance butt) and flash welding (ISO 15614-13:2012) |
NF EN ISO 25239-5 : 2012 | FRICTION STIR WELDING - ALUMINIUM - PART 5: QUALITY AND INSPECTION REQUIREMENTS |
10/30217417 DC : 0 | BS EN ISO 15614-13 - SPECIFICATION AND QUALIFICATION OF WELDING PROCEDURES FOR METALLIC MATERIALS - WELDING PROCEDURE TEST - PART 13: RESISTANCE BUTT (UPSET) AND FLASH WELDING |
13/30266359 DC : 0 | BS EN ISO 15614-1 - SPECIFICATION AND QUALIFICATION OF WELDING PROCEDURES FOR METALLIC MATERIALS - WELDING PROCEDURE TEST - PART 1: ARC AND GAS WELDING OF STEELS AND ARC WELDING OF NICKEL AND NICKEL ALLOYS |
07/30171123 DC : DRAFT AUG 2007 | BS EN ISO 25239-5 - FRICTION STIR WELDING - ALUMINIUM - PART 5: QUALITY AND INSPECTION REQUIREMENTS |
I.S. EN ISO 15614-1:2017 | SPECIFICATION AND QUALIFICATION OF WELDING PROCEDURES FOR METALLIC MATERIALS - WELDING PROCEDURE TEST - PART 1: ARC AND GAS WELDING OF STEELS AND ARC WELDING OF NICKEL AND NICKEL ALLOYS (ISO 15614-1:2017, CORRECTED VERSION 2017-10-01) |
BS EN ISO 15614-7:2016 | Specification and qualification of welding procedures for metallic materials. Welding procedure test Overlay welding |
UNI EN ISO 15614-14 : 2013 | SPECIFICATION AND QUALIFICATION OF WELDING PROCEDURES FOR METALLIC MATERIALS - WELDING PROCEDURE TEST - PART 14: LASER-ARC HYBRID WELDING OF STEELS, NICKEL AND NICKEL ALLOYS |
BS EN ISO 15614-1:2017 | Specification and qualification of welding procedures for metallic materials. Welding procedure test Arc and gas welding of steels and arc welding of nickel and nickel alloys |
EN 13445-4 : 2014 COR 2017 | UNFIRED PRESSURE VESSELS - PART 4: FABRICATION |
DIN EN ISO 15614-13:2012-10 | Specification and qualification of welding procedures for metallic materials - Welding procedure test - Part 13: Upset (resistance butt) and flash welding (ISO 15614-13:2012) |
DIN EN ISO 17642-3 E : 2005 | DESTRUCTIVE TESTS ON WELDS IN METALLIC MATERIALS - COLD CRACKING TESTS FOR WELDMENTS - ARC WELDING PROCESSES - PART 3: EXTERNALLY LOADED TESTS |
DIN EN ISO 17642-2 E : 2005 | DESTRUCTIVE TESTS ON WELDS IN METALLIC MATERIALS - COLD CRACKING TESTS FOR WELDMENTS - ARC WELDING PROCESSES - PART 2: SELF-RESTRAINT TESTS |
ONORM EN ISO 25239-5 : 2012 | FRICTION STIR WELDING - ALUMINIUM - PART 5: QUALITY AND INSPECTION REQUIREMENTS (ISO 25239-5:2011) |
I.S. EN ISO 15614-8:2016 | SPECIFICATION AND QUALIFICATION OF WELDING PROCEDURES FOR METALLIC MATERIALS - WELDING PROCEDURE TEST - PART 8: WELDING OF TUBES TO TUBE-PLATE JOINTS (ISO 15614-8:2016) |
I.S. EN ISO 15614-13:2012 | SPECIFICATION AND QUALIFICATION OF WELDING PROCEDURES FOR METALLIC MATERIALS - WELDING PROCEDURE TEST - PART 13: UPSET (RESISTANCE BUTT) AND FLASH WELDING (ISO 15614-13:2012) |
00/708223 DC : DRAFT MAY 2000 | BS EN ISO 15614-9 - SPECIFICATION AND APPROVAL OF WELDING PROCEDURES FOR METALLIC MATERIALS - WELDING PROCEDURE TEST - PART 9: UNDERWATER HYPERBARIC WET WELDING |
13/30266377 DC : 0 | BS EN ISO 15614-7 - SPECIFICATION AND QUALIFICATION OF WELDING PROCEDURES FOR METALLIC MATERIALS - WELDING PROCEDURE TEST - PART 7: OVERLAY WELDING |
BS EN ISO 9015-2:2016 | Destructive tests on welds in metallic materials. Hardness testing Microhardness testing of welded joints |
UNE-EN ISO 9015-2:2016 | Destructive tests on welds in metallic materials - Hardness testing - Part 2: Microhardness testing of welded joints (ISO 9015-2:2016) |
DIN EN ISO 25239-5:2012-03 | FRICTION STIR WELDING - ALUMINIUM - PART 5: QUALITY AND INSPECTION REQUIREMENTS (ISO 25239-5:2011) |
I.S. EN ISO 25239-5:2011 | FRICTION STIR WELDING - ALUMINIUM - PART 5: QUALITY AND INSPECTION REQUIREMENTS (ISO 25239-5:2011) |
DIN EN ISO 17642-3:2005-09 | Destructive tests on welds in metallic materials - Cold cracking tests for weldments - Arc welding processes - Part 3: Externally loaded tests (ISO 17642-3:2005) |
BS EN ISO 17642-2:2005 | Destructive tests on welds in metallic materials. Cold cracking tests for weldments. Arc welding processes Self-restraint tests |
DIN EN ISO 17642-2:2005-09 | Destructive tests on welds in metallic materials - Cold cracking tests for weldments - Arc welding processes - Part 2: Self-restraint tests (ISO 17642-2:2005) |
ISO 9015-2:2016 | Destructive tests on welds in metallic materials Hardness testing Part 2: Microhardness testing of welded joints |
EN ISO 25239-5:2011 | Friction stir welding - Aluminium - Part 5: Quality and inspection requirements (ISO 25239-5:2011) |
UNE-EN 13445-4:2015 | Unfired pressure vessels - Part 4: Fabrication |
EN ISO 17642-3:2005 | Destructive tests on welds in metallic materials - Cold cracking tests for weldments - Arc welding processes - Part 3: Externally loaded tests (ISO 17642-3:2005) |
ONORM EN ISO 15614-13 : 2012 | SPECIFICATION AND QUALIFICATION OF WELDING PROCEDURES FOR METALLIC MATERIALS - WELDING PROCEDURE TEST - PART 13: UPSET (RESISTANCE BUTT) AND FLASH WELDING (ISO 15614-13:2012) |
BS EN ISO 25239-5:2011 | Friction stir welding. Aluminium Quality and inspection requirements |
UNI EN ISO 25239-5 : 2012 | FRICTION STIR WELDING - ALUMINIUM - PART 5: QUALITY AND INSPECTION REQUIREMENTS |
PREN 12972 : DRAFT 2017 | TANKS FOR TRANSPORT OF DANGEROUS GOODS - TESTING, INSPECTION AND MARKING OF METALLIC TANKS |
BS EN ISO 15614-14:2013 | Specification and qualification of welding procedures for metallic materials. Welding procedure test Laser-arc hybrid welding of steels, nickel and nickel alloys |
03/106174 DC : DRAFT APR 2003 | ISO 22826 - DESTRUCTIVE TESTS ON WELDS IN METALLIC MATERIALS - HARDNESS TESTING OF NARROW WELDED JOINTS BY LASER AND ELECTRON BEAM (VICKERS AND KNOOP HARDNESS TESTS) |
BS ISO 22826:2005 | Destructive tests on welds in metallic materials. Hardness testing of narrow joints welded by laser and electron beam (Vickers and Knoop hardness tests) |
DIN EN ISO 15614-7:2015-01 (Draft) | SPECIFICATION AND QUALIFICATION OF WELDING PROCEDURES FOR METALLIC MATERIALS - WELDING PROCEDURE TEST - PART 7: OVERLAY WELDING (ISO 15614-7:2016) |
ISO 13847:2013 | Petroleum and natural gas industries — Pipeline transportation systems — Welding of pipelines |
16/30336547 DC : 0 | BS EN 16602-70-39 - SPACE PRODUCT ASSURANCE - PART 70-39: WELDING OF METALLIC MATERIALS FOR FLIGHT HARDWARE |
UNE-EN ISO 15614-1:2018 | Specification and qualification of welding procedures for metallic materials - Welding procedure test - Part 1: Arc and gas welding of steels and arc welding of nickel and nickel alloys (ISO 15614-1:2017, Corrected version 2017-10-01) |
17/30360691 DC : 0 | BS EN 12972 - TANKS FOR TRANSPORT OF DANGEROUS GOODS - TESTING, INSPECTION AND MARKING OF METALLIC TANKS |
UNE-EN ISO 15614-7:2017 | Specification and qualification of welding procedures for metallic materials - Welding procedure test - Part 7: Overlay welding (ISO 15614-7:2016) |
ISO 15614-7:2016 | Specification and qualification of welding procedures for metallic materials Welding procedure test Part 7: Overlay welding |
ISO 25239-5:2011 | Friction stir welding Aluminium Part 5: Quality and inspection requirements |
ISO 15614-14:2013 | Specification and qualification of welding procedures for metallic materials — Welding procedure test — Part 14: Laser-arc hybrid welding of steels, nickel and nickel alloys |
ISO 15614-13:2012 | Specification and qualification of welding procedures for metallic materials Welding procedure test Part 13: Upset (resistance butt) and flash welding |
ISO 17642-3:2005 | Destructive tests on welds in metallic materials — Cold cracking tests for weldments — Arc welding processes — Part 3: Externally loaded tests |
UNE-EN ISO 15614-8:2016 | Specification and qualification of welding procedures for metallic materials - Welding procedure test - Part 8: Welding of tubes to tube-plate joints (ISO 15614-8:2016) |
UNE-EN ISO 15614-13:2013 | Specification and qualification of welding procedures for metallic materials - Welding procedure test - Part 13: Upset (resistance butt) and flash welding (ISO 15614-13:2012) |
ISO 17642-2:2005 | Destructive tests on welds in metallic materials — Cold cracking tests for weldments — Arc welding processes — Part 2: Self-restraint tests |
BS EN ISO 17642-3:2005 | Destructive tests on welds in metallic materials. Cold cracking tests for weldments. Arc welding processes Externally loaded tests |
BS EN ISO 15614-8:2016 | Specification and qualification of welding procedures for metallic materials. Welding procedure test Welding of tubes to tube-plate joints |
EN ISO 17642-2:2005 | Destructive tests on welds in metallic materials - Cold cracking tests for weldments - Arc welding processes - Part 2: Self-restraint tests (ISO 17642-2:2005) |
EN ISO 15614-14:2013 | Specification and qualification of welding procedures for metallic materials - Welding procedure test - Part 14: Laser-arc hybrid welding of steels, nickel and nickel alloys (ISO 15614-14:2013) |
EN ISO 15614-8:2016 | Specification and qualification of welding procedures for metallic materials - Welding procedure test - Part 8: Welding of tubes to tube-plate joints (ISO 15614-8:2016) |
15/30311766 DC : 0 | BS ISO 9015-2 - DESTRUCTIVE TESTS ON WELDS IN METALLIC MATERIALS - HARDNESS TESTING - PART 2: MICROHARDNESS TESTING OF WELDED JOINTS |
API 2SF : 2013 | MANUFACTURE OF STRUCTURAL STEEL FORGINGS FOR PRIMARY OFFSHORE APPLICATIONS |
UNE-EN ISO 15614-14:2014 | Specification and qualification of welding procedures for metallic materials - Welding procedure test - Part 14: Laser-arc hybrid welding of steels, nickel and nickel alloys (ISO 15614-14:2013) |
I.S. EN ISO 9015-2:2016 | DESTRUCTIVE TESTS ON WELDS IN METALLIC MATERIALS - HARDNESS TESTING - PART 2: MICROHARDNESS TESTING OF WELDED JOINTS (ISO 9015-2:2016) |
I.S. EN ISO 15614-14:2013 | SPECIFICATION AND QUALIFICATION OF WELDING PROCEDURES FOR METALLIC MATERIALS - WELDING PROCEDURE TEST - PART 14: LASER-ARC HYBRID WELDING OF STEELS, NICKEL AND NICKEL ALLOYS (ISO 15614-14:2013) |
ISO 15614-1:2017 | Specification and qualification of welding procedures for metallic materials — Welding procedure test — Part 1: Arc and gas welding of steels and arc welding of nickel and nickel alloys |
BS EN 13445-4 : 2014 | UNFIRED PRESSURE VESSELS - PART 4: FABRICATION |
BS EN ISO 15614-13:2012 | Specification and qualification of welding procedures for metallic materials. Welding procedure test Upset (resistance butt) and flash welding |
ISO 15614-8:2016 | Specification and qualification of welding procedures for metallic materials — Welding procedure test — Part 8: Welding of tubes to tube-plate joints |
EN ISO 9015-2:2016 | DESTRUCTIVE TESTS ON WELDS IN METALLIC MATERIALS - HARDNESS TESTING - PART 2: MICROHARDNESS TESTING OF WELDED JOINTS (ISO 9015-2:2016) |
UNI EN ISO 15614-13 : 2012 | SPECIFICATION AND QUALIFICATION OF WELDING PROCEDURES FOR METALLIC MATERIALS - WELDING PROCEDURE TEST - PART 13: UPSET (RESISTANCE BUTT) AND FLASH WELDING |
ISO 6507-1:2005 | Metallic materials Vickers hardness test Part 1: Test method |
ISO 6506-1:2014 | Metallic materials Brinell hardness test Part 1: Test method |
ISO 9015-2:2016 | Destructive tests on welds in metallic materials Hardness testing Part 2: Microhardness testing of welded joints |
Please Login or Create an Account so you can add users to your Multi user PDF Later.
Important note : Users cannot be edited or removed once added to your Multi user PDF.
Access your standards online with a subscription
Features
-
Simple online access to standards, technical information and regulations.
-
Critical updates of standards and customisable alerts and notifications.
-
Multi-user online standards collection: secure, flexible and cost effective.