IEC 61249-2-26:2005
Current
The latest, up-to-date edition.
![header thumbnail](/images/publishers\iec_cover.gif)
Materials for printed boards and other interconnecting structures - Part 2-26: Reinforced base materials clad and unclad - Non-halogenated epoxide non-woven/woven E-glass reinforced laminated sheets of defined flammability (vertical burning test), copper-clad
Hardcopy , PDF , PDF 3 Users , PDF 5 Users , PDF 9 Users
English - French
11-01-2005
FOREWORD
1 Scope
2 Normative references
3 Materials and construction
3.1 Resin system
3.2 Reinforcement
3.3 Metal foil
4 Internal marking
5 Electrical Properties
6 Non-Electrical properties of the copper-clad laminate
6.1 Appearance of the copper-clad sheet
6.2 Appearance of the unclad face
6.3 Laminate Thickness
6.4 Bow and twist
6.5 Properties related to the copper foil bond
6.6 Punching and machining
6.7 Dimensional stability
6.8 Sheet sizes
6.9 Cut panels
7 Non-electrical properties of the base material after
complete removal of the copper foil
7.1 Appearance of the dielectric base material
7.2 Flexural Strength
7.3 Flammability
7.4 Water absorption
7.5 Measling
7.6 Glass transition temperature and cure factor
8 Quality assurance
8.1 Quality system
8.2 Responsibility for inspection
8.3 Qualification inspection
8.4 Quality conformance inspection
8.5 Certificate of conformance
9 Packaging and marking
10 Ordering information
Annex A (informative) Engineering information
Annex B (informative) Common laminate constructions
Annex C (informative) Guideline for qualification and
conformance inspection
This part of IEC 61249 gives requirements for properties of non-halogenated epoxide non-woven/woven reinforced E-glass laminated sheets of defined flammability (vertical burning test), copper-clad in thicknesses of 0,80 mm up to 1,60 mm. The flammability rating is achieved through the use of non-halogenated inorganic and/or organic compounds acting as fire retardants. These fire retardants are contained as part of polymeric structure or in addition to it. The glass transition temperature is defined to be 95 °C minimum.
Committee |
TC 91
|
DevelopmentNote |
Stability Date: 2020. (09/2017)
|
DocumentType |
Standard
|
Pages |
45
|
PublisherName |
International Electrotechnical Committee
|
Status |
Current
|
Standards | Relationship |
NF EN 61249-2-26 : 2005 | Identical |
NEN EN IEC 61249-2-26 : 2005 | Identical |
I.S. EN 61249-2-26:2005 | Identical |
PN EN 61249-2-26 : 2005 | Identical |
UNE-EN 61249-2-26:2005 | Identical |
BS EN 61249-2-26:2005 | Identical |
CEI EN 61249-2-26 : 2005 | Identical |
EN 61249-2-26:2005 | Identical |
DIN EN 61249-2-26:2005-08 | Identical |
IEC PAS 63015:2016 | Definition of "Low-Halogen" for electronic products |
PD IEC/PAS 63015:2016 | Definition of “Low-Halogen” for electronic products |
ISO 11014-1:1994 | Safety data sheet for chemical products Part 1: Content and order of sections |
IEC 61249-5-1:1995 | Materials for interconnection structures - Part 5: Sectional specification set for conductive foils and films with and without coatings - Section 1: Copper foils (for the manufacture of copper-clad base materials) |
ISO 14001:2015 | Environmental management systems — Requirements with guidance for use |
IEC 60194:2015 | Printed board design, manufacture and assembly - Terms and definitions |
ISO 9000:2015 | Quality management systems — Fundamentals and vocabulary |
IEC 61189-2:2006 | Test methods for electrical materials, printed boards and other interconnection structures and assemblies - Part 2: Test methods for materials for interconnection structures |
Access your standards online with a subscription
Features
-
Simple online access to standards, technical information and regulations.
-
Critical updates of standards and customisable alerts and notifications.
-
Multi-user online standards collection: secure, flexible and cost effective.