MIL-PRF-85582 Revision E:2012
Current
Current
The latest, up-to-date edition.
PRIMER COATINGS: EPOXY, WATERBORNE
Available format(s)
PDF
Language(s)
English
Publisher
Important note : Users cannot be edited or removed once added to your Multi user PDF.
1. SCOPE
2. APPLICABLE DOCUMENTS
3. REQUIREMENTS
4. VERIFICATION
5. PACKAGING
6. NOTES
Provides the requirements for corrosion inhibiting, chemical and solvent resistant, waterborne, epoxy primer coatings that have a maximum volatile organic compound (VOC) content of 340 grams per liter (g/L) (2.8 pounds per gallon [lb/gal]).
| Committee |
FSC 8010
|
| DevelopmentNote |
Supersedes MIL P 85582 (B). (08/2002)
|
| DocumentType |
Standard
|
| Pages |
18
|
| ProductNote |
NEW CHILD NOT 1 2019 IS NOW ADDED.
|
| PublisherName |
US Military Specs/Standards/Handbooks
|
| Status |
Current
|
| Supersedes |
| MIL-DTL-53072 Revision F:2017 | CHEMICAL AGENT RESISTANT COATING (CARC) SYSTEM - APPLICATION PROCEDURES AND QUALITY CONTROL INSPECTION |
| SAE AMS2477A | Conversion Coating for Aluminum Alloys Low Electrical Resistance Coating |
| MIL-PRF-32405 Base Document:2013 | CLEANER, HAND WIPE, FOR AVIATION AND MISSILE SYSTEMS, METALLIC SUBSTRATES, LOW OR EXEMPT VOC |
| SAE AMS3166C | Solvents, Cleaning, Cleaning Prior to Application of Sealing Compounds |
| SAE AIR 5479 : 2017 | ENVIRONMENTALLY COMPLIANT PROCESSES FOR LANDING GEAR |
| MIL-PRF-22750 Revision G:2011 | COATING, EPOXY, HIGH-SOLIDS |
| MIL-PRF-85322 Revision C:2014 | COATING, ELASTOMERIC, POLYURETHANE, RAIN-EROSION |
| SAE AMS3278B | Sealing and Coating Compound, Polyurethane (PUR) Fuel Resistant High Tensile Strength / Elongation For Integral Fuel Tanks / Fuel Cavities / General Purpose |
| SAE AMS3167B | Solvents, Wipe for Cleaning Prior to Application of Primer and Top Coat Materials, or Sealing Compounds |
| SAE AMS2480H | Phosphate Treatment Paint Base |
| SAE AMS3255B | Sealing Tape, Sheet, or Gasket, Polytetrafluoroethylene, Expanded (EPTFE) Oil and Water Resistant |
| SAE AMS3379 | Sealing Compound, Polysulfide Rubber Preformed Strips for Sealing Removable Doors, Skins, and Panels |
| MIL-DTL-14072 Revision F:2013 | FINISHES FOR GROUND BASED ELECTRONIC EQUIPMENT |
| AWWA C218:2023 | Liquid Coatings for Aboveground SteelWater Pipe and Fittings |
| P-W-2891 Revision A:2002 | WIPE SOLVENTS, EXEMPT AND NON-EXEMPT |
| SAE AMS3276F | Sealing Compound, Integral Fuel Tanks and General Purpose, Intermittent Use to 360 °F (182 °C) |
| SAE AMS3102 | Sealing Compound, Polythioether Rubber Fast Curing, Light Weight (Specific Gravity 0.78, max.) for Integral Fuel Tanks and General Purpose, Intermittent Use to 360 °F (182 °C) |
| SAE AS5127B | Aerospace Standard Test Methods for Aerospace Sealants Methods for Preparing Aerospace Sealant Test Specimens |
| MIL-PRF-81352 Revision C:2005 | COATINGS, AIRCRAFT TOUCH-UP |
| MIL-STD-186 Revision F:2002 | PROTECTIVE FINISHING SYSTEMS FOR ROCKETS, GUIDED MISSILES, SUPPORT EQUIPMENT AND RELATED MATERIALS |
| SAE AMS3100D | Adhesion Promoter For Polysulfide Sealing Compounds |
| SAE AMS3265E | Sealing Compound, Polysulfide (T) Rubber, Fuel Resistant, Non-Chromated Corrosion Inhibiting For Intermittent Use to 360 °F (182 °C) |
| MIL-PRF-85285 Revision E:2012 | COATING: POLYURETHANE, AIRCRAFT AND SUPPORT EQUIPMENT |
| MIL-DTL-32459 Base Document:2013 | Coatings, Anodic for Magnesium and Magnesium Alloys |
| MIL-DTL-18264 Revision E:2015 | FINISHES, ORGANIC, WEAPONS SYSTEMS, APPLICATION AND CONTROL OF |
| MIL-DTL-27516 Revision G:2011 | Hose and Hose Assembly, Nonmetallic, Suction and Discharge |
| MIL-DTL-5541 Revision F:2006 | Chemical Conversion Coatings on Aluminum and Aluminum Alloys |
| MIL-STD-7179 Revision A:2009 | Finishes, Coatings, and Sealants, for the Protection of Aerospace Weapons Systems and Support Equipment |
| MIL-DTL-6615 Revision G:2008 | Hose Assemblies, Rubber, Fuel and Nonpotable Water, with Reattachable Couplings, Low Temperature, General Specification for |
| MIL-STD-171 Revision F:2011 | FINISHING OF METAL AND WOOD SURFACES |
| SAE AMS3281F | Sealing Compound, Polysulfide (T) Synthetic Rubber for Integral Fuel Tank and Fuel Cell Cavities Low Density for Intermittent Use to 360 °F (182 °C) |
| MIL-STD-2161 Revision C:2014 | Paint Schemes and Exterior Markings for U.S. Navy and Marine Corps Aircraft |
| MIL-DTL-64159 Revision B:2011 | CAMOUFLAGE COATING, WATER DISPERSIBLE ALIPHATIC POLYURETHANE, CHEMICAL AGENT RESISTANT |
| SAE AMS3603A | Protective Film, High Performance, Polymeric Pressure Sensitive Adhesive, for Aircraft Exterior Applications |
| MIL-DTL-81706 Revision B:2004 | Chemical Conversion Materials for Coating Aluminum and Aluminum Alloys |
| SAE AMS2473H | Chemical Film Treatment for Aluminum Alloys General Purpose Coating |
| SAE AS5127/1C | Aerospace Standard Test Methods for Aerospace Sealants Two-Component Synthetic Rubber Compounds |
| MIL-DTL-53039 Revision E:2013 | COATING, ALIPHATIC POLYURETHANE, SINGLE COMPONENT, CHEMICAL AGENT RESISTANT |
| MIL-PRF-32587 Base Document:2018 | Remover, Paint, Hap-Free, Neutral |
| MIL-PRF-87937 Revision D:2001 | CLEANING COMPOUND, AEROSPACE EQUIPMENT |
| MIL-DTL-85054 Revision D:2010 | CORROSION PREVENTIVE COMPOUND, WATER-DISPLACING, TRANSPARENT (FORMERLY AMLGUARD) |
| SAE AMS3277J | Sealing Compound, Polythioether Rubber Fast Curing for Integral Fuel Tanks and General Purpose, Intermittent Use to 360 °F (182 °C) |
| SAE AMS3144 | Primer, Anodic Electrodeposition for Aircraft Applications |
| MIL-STD-1568 Revision D:2015 | Materials and Processes for Corrosion Prevention and Control in Aerospace Weapons Systems |
| SAE ARP4118A | Isolation and Corrosion Protection of Dissimilar Materials, Carbon Composite Structure Repair |
| SAE AMS3092A | Release Agent, for Use During Form-In-Place Gasket Preparation |
| SAE AMS1640B | Corrosion Removing Compound For Aircraft Surfaces |
| ASTM D 823 : 1995 | Standard Practices for Producing Films of Uniform Thickness of Paint, Varnish, and Related Products on Test Panels |
| ASTM D 5895 : 2013 : REDLINE | Standard Test Methods for Evaluating Drying or Curing During Film Formation of Organic Coatings Using Mechanical Recorders |
| MIL-PRF-85285 Revision E:2012 | COATING: POLYURETHANE, AIRCRAFT AND SUPPORT EQUIPMENT |
| SAE AMSQQA250/4B | Aluminum Alloy 2024, Plate and Sheet |
| ASTM D 1200 : 2010 | Standard Test Method for Viscosity by Ford Viscosity Cup |
| MIL-DTL-5541 Revision F:2006 | Chemical Conversion Coatings on Aluminum and Aluminum Alloys |
| TT-R-2918 Revision A:2001 | REMOVAL, PAINT, NO HAZARDOUS AIR POLLUTANTS (HAPS) |
| MIL-C-8514 Revision C:1967 | COATING, COMPOUND, METAL PRETREATMENT, RESIGN ACID [ASG] |
| MIL-R-81294 Revision D:1990 | REMOVER, PAINT, EPOXY, POLYSULPHIDE AND POLYURETHANE SYSTEMS |
| MIL-PRF-23699 Revision G:2014 | Lubricating Oil, Aircraft Turbine Engine, Synthetic Base, NATO Code Numbers: O-152, O-154, O-156, and O-167 |
| SAE AMSQQA250/5B | Aluminum Alloy Alclad 2024, Plate and Sheet |
| MIL A 8625 : F | ANODIC COATINGS FOR ALUMINUM AND ALUMINUM ALLOYS |
| MIL-PRF-83282 Revision D:1997 | HYDRAULIC FLUID, FIRE RESISTANT, SYNTHETIC HYDROCARBON BASE, METRIC, NATO CODE NUMBER H-537 |
| FED-STD-141 Revision D:2001 | PAINT, VARNISH, LACQUER AND RELATED MATERIALS, METHODS OF INSPECTION, SAMPLING AND TESTING |
| FED-STD-595 Revision C:2008 | COLORS USED IN GOVERNMENT PROCUREMENT |
| ASTM D 3359 : 2017 : REDLINE | Standard Test Methods for Rating Adhesion by Tape Test |
Access your standards online with a subscription
Features
-
Simple online access to standards, technical information and regulations.
-
Critical updates of standards and customisable alerts and notifications.
-
Multi-user online standards collection: secure, flexible and cost effective.